UGC Insulating Firebrick (IFB) is a lightweight, high-porosity (typically 50%-80%)refractory brick made from alumina and silica that is designed to withstand high temperatures while providing excellent thermal insulation and low heat conductivity. Its low thermal conductivity minimizes heat loss in furnaces, kilns, and other high-temperature applications, making it energy-efficient. The porous structure is created by adding an organic filler that burns away during manufacturing, and the bricks are soft enough to be easily cut with standard hand tools for custom shapes
Physical Properties:
Low thermal conductivity
High-Temperature Resistance
Low Density and Lightweight
Adequate Mechanical Strength
Low linear shrinkage
Chemical Resistance
Typical Application:
Industry Furnaces and Kilns
Power Generation boilers, exhaust systems
Aerospace black boxes
Wood stoves&ovens&barbecues
Laboratory furnaces, incinerators
|
Description |
GRADE 23 BRICK |
GRADE 26 BRICK |
GRADE 28 BRICK |
GRADE 30 BRICK |
|
Classification Temperature(℃) |
1300 |
1400 |
1500 |
1550 |
|
Chemical Composition(%) |
||||
|
Al₂O₃ |
40 |
56 |
67 |
73 |
|
SiO₂ |
51 |
41 |
30 |
24 |
|
Fe₂O₃ |
≤1.0 |
≤0.8 |
≤0.7 |
≤0.6 |
|
Density(kg/m³) |
600 |
800 |
900 |
1000 |
|
Modulus of Rupture(MPa) |
0.9 |
1.5 |
1.8 |
2 |
|
Cold Crushing Strength(MPa) |
1.2 |
2.4 |
2.6 |
3 |
|
Permanent Linear Change(%) |
1230℃×24h≤0.3 |
1400℃×24h≤0.6 |
1510℃x24h≤0.7 |
1620℃×24h≤0.9 |
|
Thermal Conductivity (W/m ·K) |
||||
|
200℃ |
0.15 |
0.23 |
0.27 |
0.28 |
|
350℃ |
0.18 |
0.24 |
0.3 |
0.35 |
|
400℃ |
0.19 |
0.25 |
0.33 |
0.38 |
|
600℃ |
0.23 |
0.27 |
0.38 |
0.4 |